1.Product Description
Double Coated Tape with a thin polyester film for dimensional stability and improved handling with ease of die cutting and laminating. The high tack adhesive provides relatively high initial
adhesion and good shear holding power to a variety of surfaces.
2.Construction
EP 5520 | |
Face side 1 Adhesive Type/Thickness | Acrylate/0.0007(0.018mm) |
Backside 2 Adhesive Type/Thickness | Acrylate/0.0007(0.018mm) |
Liner Color,Type | White,55#SCK,No print |
Liner Caliper | 0.003(0.076mm) |
Carrier Type | Clear PET 3/0.0005(0.012mm) |
Note 1:Faceside adhesive is on the interior of the roll,exposed when unwound. 2:Backside adhesive is on the exterior of the roll,exposed when liner is removed. 3:PET(Polyester) | |
3. Typical Physical Note : The following technical information and data should be considered representative or typical only and should not be used for
Properties and specification purposes.
Performance
Characteristics
EP5520 | ||||
Adhesion to stainless steel | 15 minutes RT | 70(N/100mm) | ||
72 hours RT | 76(N/100mm) | |||
Adhesion to PET | 15 minutes RT | 65(N/100mm) | ||
Adhesion to other surfaces | 15 minutes RT | ABS | 60(N/100mm) | |
Polycarbonate | 65(N/100mm) | |||
SheartStrength-ASTM D3654 (1 inch2 sample size)1000grams at 72(22) | 10000 minutes | |||
Relative solvent resistance | Medium-Low | |||
UV Resistance | Medium | |||
Relative High Temperature | Operating Ranges | Long Term(days,week) 80 | ||
Short Term(minutes,hours)150 | ||||
Shelf Life of Tape in Roll Form | 24 months from date of manufacture when stored in original cartons at 70(21) and 50% relative humidity | |||
4. Application Bond strength is dependent upon the amount of adhesive-to-surface
Techniques contact developed. Firm application pressure helps develop better adhesive contact and improves bond strength.
To obtain optimum adhesion, the bonding surfaces must be clean,
dry and well unified. Some typical surface cleaning solvents are isopropyl alcohol or heptane.
Note: Carefully read and follow the manufacturers precautions and directions for use when working with solvents.
Ideal tape application temperature range is 70°F to 100°F (21°C to38°C). Initial tape application to surfaces at temperatures below 50°F (10°C) is not recommended because the adhesive becomes too firm to adhere readily. However, once properly applied, low temperature holding is generally satisfactory.
5.General All tapes have a film carrier, which can add dimensional stability to
Information foams and other substrates. The carrier also provides easier handling during slitting and die-cutting.
6.Features Adhesive is a medium-firm acrylic adhesive system featuring both high initial adhesion and good high temperature holding power.
7.Application Medical/non-medical diagnostic test strips
Ideas Plastic film lamination/bonding
Splicing
Foam lamination
8.Application To apply adhesives in a wide web format, lamination equipment is
Equipment required to ensure acceptable quality. To learn more about working with pressure-sensitive adhesives please refer to technical bulletin, Lamination Techniques for Converters of Laminating Adhesives.
9.Certification/ MSDS: has prepared a MSDS for the products.
Recognition TSCA: The product are defined as articles under the Toxic Substances Control Act and therefore,are exempt from inventory listing requirements.
ISO9001 ISO14001 |
This Engineered Adhesives Division product was manufactured under a quality system registered to ISO 9001 standards and Environmental system registered to ISO 14001 standards.
EP-5520 Double sided tape with Thin PET (substitute for 3M444)