Characteristics:
1. Solvent free: don’t produce any volatile compound. Outstanding thixotropism, suitable for all-wave
construction.
2. Low tack: construction craftwork is simple and improve efficiency, cost reduction. After solidification, it form
elastomer,which has excellent cohesion to glass and aluminum alloy etc metal.
3. Suitable for all kinds of climate: it could keep its characteristics from -50°C to 100°C and could construct
from -5°C to 45°C. It has compatibility with all kinds of hot melt butyl, suitable for the manufacture of double
timessealing of insulating glass.
Technical Data Sheet:
The following data only for reference.
No | Item | Technical data | product quality index | ||
1 | Appearance | A component | White paste | White paste | |
B component | Black paste | Black paste | |||
2 | Pulling and bond strength(Mpa) 72h | ≥0.6 | ≥0.6 | ||
3 | Suitable period 30 min,S | ≤10 | 2.8 | ||
4 | Surface dry time | ≤2 | 1.0 | ||
5 | slump | vertical placement | ≤3 | 1 | |
horizontal placement | No distortion
| No distortion
| |||
6 | hardness(A) 24h | 20-60 30 | |||
Note: the above experiment condition is 24±0.2°C, mix proportion A:B = 10:1 | |||||
The products is according to the JC/T486-2001 which is according to PS 12.5E. | |||||
Two component polysulfide sealant