Product Name

Shock Absorber Rod Guide

Raw Materials

MPIF FC-0205

Feature

1. Density from 6.5-6.7 g/cm32. Hardness: HRB 60-1003. Steam treatment: 2H high temp steam holding time, Thickness of Fe3O4: 0.004-0.005mm4. Full line products for shock absorber, including powder metallurgy piston, rod guide, 

foot valve, PTFE band for piston, Du bearing for rod guide.5. PPAP III is submitted accordingly.

Application

Car shock absorber, Motorcycle shock absorber, Bicycle shock absorber

Processing

Mixing powder——Forming——Sintering——Sizing——After treatment——Steam treatment——Oil impregnant——Packing——Shipping

Manufacturability

1. Auto Mechanical Press: 50T, 100T, 140T2. Hydraulic Press: 100T, 315T, 600T, 800T3. Six sinter furnaces, including one harden Sinter Furnace4. Heat treatment: Carbonitriding quenching and high frequency quenching5. Ultrasonic clearing and auto deburring6. In-house tooling making: EDM, wire cutting machine7. Strength in machining: Machine center, CNC milling, CNC lathe, Two end lapper etc. 

Test Ability.

1. Carbon selfur determinator2. Metallurgic microscope3. Hydraulic universal material tester4. Hardness testers5. Pneumatic measuring instrument6. Measuring projector7. Gear testing instrument8. Electrical profilometer9. CMM

QMS

ISO9001, ISO/TS16949;ISO14001

Advantage

1. Well experienced OEM manufacturer2. 25 years in the powder metallurgy industry

3. Professional technology service4. Familiar with automobile industry requirement.