SiO2

 min94.5%

 Al2O3

 max 1.5%

 Fe2O3

 max 1.5%

 CaO

 max 2.5%

 Apparent porosity

 max 22(24)%

 CCS MPa

 min40(35)

 0.2 Mpa refractoriness under load,  °C

 min 1650

 Reheating linear change,%,1450°C*2h

 from 0 to 2

 True density

 2.33(2.34)g/cm3

 Residual quartz

 max 1.0%

 Thermal expansion rate (1000°C)%

 1.28