cast iron casting steel grinding ball 1) High hardness 2) Low breakage 3) Good wear-resistant 4) Steady performance

1.Chemical composition:

  

Casted grinding ball

Item	C	Cr	Si	Mn	S	P	Cu	Mo	Hardness
Low Chrome	1.8-3.5	1-3.5	≤1.2	≤1.5	≤0.15	≤0.15	≤0.5	≤1.0	≥45
Medium Chrome	1.8-3.3	4-9	≤1.2	≤1.8	≤0.15	≤0.15	≤1.0	≤1.5	≥50
High Chrome	1.6-3.3	10-15	≤1.0	≤2.5	≤0.10	≤0.10	≤1.5	≤1.0	≥55
Higher Chrome	1.6-3.3	15-18 18-27	≤1.0	≤2.5	≤0.10	≤0.10	≤1.5	<2.0	≥60

 2.Features:

(1) Characteristics: a) High hardness and resistance b) Good even wear c) No breaking

(2) Applied fields: a) Miningb) Cement plants c) Power stations d) Chemical industry and machinery

Production Process

The production of casting steel balls is to melt the waste raw material such as waste steel, waste iron with medium frequency induction furnace. In the process of melting, add suitable amount of precious metal alloys(such as Ferrochrome, ferromanganese, ferro-vanadium ) to the furnace. When the temperature of the molten iron is more than 1550°C and can meet the requirements of the technics,pour the qualified molten iron to steel moulds or steel production line moulds. The content of chrome of high chrome alloy casting steel balls is ≥10.0%, the content of carbon is 1.80%-3.20%. Since the national standards require the HRC≥58, ak≥3.0J/cm2, to up to this hardness, the high chrome balls must be quenched and tempered. After quenched and tempered, the hardness(HRC≥60) is higher, the wear-resistance is more than 2.5 times of forging balls.

Product Features: No broken, wear-resistance, round, even hardness, high efficiency for mill.

Production Technics

Raw material(waste steel,waste iron,iron alloy)factory inspection→blending→melt→composition inspection→casting→cooling and solidification→demould→clean and polish→inspection→quenching(increase hardness)→hardness inspection→tempering(eliminate stress)→inspection→warehousing

Dia 20mm cast iron casting steel grinding ball