Zinc Oxide Desulfurization Adsorbent *Desulfurization adsrobent * Zinc oxide catalyst * Remove H2S * High strength

Zinx Oxide Desulfurization Adsorbent:

HL-302 zinc oxide desulfurization adsorbent is composed of active zinc oxide, manganese oxide and magnesium 

oxide. Active zinc oxide is main component. It has the ability of good adsorption of hydrogen sulfide and converting 

the simple organic sulfur compounds. In addition, it still has good desulfurization activity at room temperature and 

the desulfurization rate can reach 99.5%.

The product which is mainly used in synthesis ammonia plant of semi-water gas as raw materials,removes the 

small amount of H2S and "reactive" organic sulfur in feed gas in low temperature shift stove to protect the low-temperature shift catalyst.                                                                                                                                                                                                                                                                                                                             

It is also used for desulfurization from natural gas, oil gas, cok-oven gas and rich gas of refinery  coking which is 

hydrogenated and of coking gas refinery.

Physical and chemical properties:

item	index	item	Index
Appearance	Dark gray sphere or extrudates	loss on Ignition, %	≤5
Particle size mm	Φ3–5 orΦ4*5-15	Zinc oxide content %	≥80
Crushing strength N/particle	≥15	manganese oxide content %	≥3
loss on abrasion %	≤6.0	Breakthrough sulfur capacity, %	≥15.0

Reference operating conditions:

Process parameters	Pressure MPa	Temperature, °C	Space velocity hr-1	Water vapor / dry air  V/V
	Normal pressure-3.0	200-350	3000	<0.3
Feed stock	Inlet sulfur (H2S)<100ppm
Output objects	Outlet total sulfur content <0.5ppm

For more details, please don't hesitate to contact with me.