Ads by Google
Application
1. Fast setting tile adhesives
2. Fast setting tile grouts
3. Shot-crete/Gun-nite
4. External renders
5. Self smoothing mortars
6. Self leveling mortars
7. Anchor bolt grouts
8. Non shrinking grouts.
Main constituents (%)
| Component | Type 1 | Type 2 | Type 3 | Type 4 | Type 5 |
| SiO2 | =<6.5 | =<8.0 | =<10.0 | ||
| Al2O3 | >=36 | >=35 | >=34 | >=32 | >=28 |
| Fe2O3 | 1.5-2.5 | 1.5-3.5 | 1.5-3.5 | ||
| CaO | 40.0-41.5 | 40.5-42.5 | 41.5-43.5 | ||
| MgO | 1.5-2.5 | =<3.0 | =<3.0 | ||
| SO3 | 9.0-11.0 | 8.5-10.5 | 8.0-9.5 | ||
| TiO2 | 1.0-2.0 | 1.0-2.0 | 1.0-2.0 |
Fineness
Specific Surface Area: according to standard GB/T 8074-1987
Usual range: 360~430 m2/kg
Specification limit: >360 m2/kg
Hydraulic Properties
The characteristics of HCSA BINDER have been tested in accordance with the Chinese standards.
1. Setting time determined at 20 using Vicat needle, according to GB/T 1346-2001
2. Mechanical strength at 20 , 95% relative humidity.
| Item | Type 1 | Type 2 | Type 3 | |
| Bending strength (MPa) | 1d | >=8.0 | >=7.0 | >=6.0 |
| Bending strength (MPa) | 3d | >=10.0 | >=9.0 | >=8.0 |
| Bending strength (MPa) | 7d | >=11.0 | >=10.0 | >=9.0 |
| Compressive strength (MPa) | 1d | >=60.0 | >=50.0 | >=50.0 |
| Compressive strength (MPa) | 3d | >=85.0 | >=75.0 | >=65.0 |
| compressive strength (MPa) | 7d | >=95.0 | >=85.0 | >=75.0 |
| Setting time (min) | initial | >=25 | >=25 | >=25 |
| Setting time (min) | Final | =<300 | =<300 | =<300 |
CSA cement