Silicone Oil for Polyester three-Dimensional Crimp Fiber for Special Smoothness
HY-8881 50±2% special type reactive Organosilicon Emulsion
HY-8882 50±2% reactive Organosilicon Emulsion
HY-8883 15±2% special type Organosilicon catalyzer and fast-dryer
HY-8884 ≥96% special type Organosilicon Cross-linking agent
About Pretreatment
a. It does not need predry
b. The proportion of the ingredients in emulsion can be adjusted according to different fiber denier.
c. Silicone oil immitting: 0.4~0.6%.
d. Speed of Hot Air ≥ 1.5m/s
Method of Application
(1) Ingredient proportion in emulsion
Silicone Oil: 1 Share (HY-8881 70 shares HY-8882 20 shares HY-8883 10 shares HY-8884 4 shares)
Water : 9~18 Shares
(2) Confection (Supposing: Water/ Silicone Oil=90kg: 10.4kg, Emulsion 104kg)
a. Immit 0.4 kg HY-8884 and 90 kg water into the oil trough, then churn it slowly for about 10 minutes.
b. Immit 7 kg HY-8881, 2 kg HY-8882, 1 kg HY-8883 into the trough in turn , then churn it for 20 minutes.
c. Application: the confected emulsion has been ready for using in fiber handling (Impregnating in Oil Through or Sprinkling).
(3) Water percentage in fiber before Torrefaction <10%
(4) Emulsion contained: 8~10%
(5) Organosilicon contained: o.4%-o.6%
(6) Torrefaction: 140ºC ~180ºC*10 minutes
(7) Temperature in the Oven:
No.1 area of oven: 150ºC
No.2 and No.3 area of oven: 160ºC
Notice
a. Techniques of using oil trough: Silicone Oil should be added in time according to the fiber output.
b. Techniques of Sprinkling
c. Water content of the fiber after Torrefaction : <0.1%
d. Quality Valid: within twelve months, keep sealed.
e. DO NOT MIX WITH ANY ANION AUXILIARY!
HY-888 Silicone Oil for Polyester Staple Fiber of three-Dimensional Crimp for Special Smoothness