Item

Unit

Standard

BJ-A

Fast Cure

BJ-B

V A Contents V A

%

30

30

Melting  Point

(before cross-linking)

72

72

Light Transmittance

%

91

91

Density

g/cm3

0.96

0.96

Specific Heat

J/·g

2.3

2.3

Heat Conductivity

W/mk

0.3

0.3

Glass Transition Temp

-40

-40

TensileStrength at Break

(after cross-linking)

Mpa

20

20

Elongation at Break

(after cross-linking)

%

560

560

Mpa

6

6

Water Absorption

(2020min) 20 20

%

0.1

0.1

Cross-linking rate

(13520min ) (13520)

%

78

82

Adhesive Strength

(First EVA-Glass)

N/20mm

103

96

Adhesive Strength

(First EVA-TPT) TPT

N/20mm

147

120

Light Resistance

(UV Radiation 800hr)UV800

Retention

95or

above

95or

above

Damp Heat Test

(1000hrat+85,85%RH)1000+85,85%

Retention

95or

above

95or

above