1) Materials: 50% -99.98% alumina oxide content 2) Application:electric heating equipment and textile machinery

1) Materials: 50% -99.98% alumina oxide content2) Application: Used for all kinds of electric heating equipment and electricEquipment, and textile machinery3) Good smooth and high strength4) A variety of specifications available5) OEM, ODM and OBM are welcomed

Features:1. High Mechanical Strength2. High Thermal Conductivity3. High Spalling Resistance4. High Softening Temperature5. Excellent Insulativity6. Etching ResistanceApplication:

Temperature measuring metersProtection and insulation for thermocouples and thermometersFurnace tube for resistance furnaces, heat treatment furnacesChemical analysis for steel and ironVarious insulationg parts for high temperature resistance and etching resistanceStructure Model:Round and ovalMono hole/single bore, double hole/twin bore and multi hole/multi boreThreadedRhombohedral

High Purity Alumina Tubes:1. Extreme high temperature stability under reducing, inert and high vacuum condition under high temperature up to 1800C. 2. Extreme wear and abrasion resistance. 3. Chemical corrosion resistance under high temperature. 4. High dielectric properties. 5. Gas tight for many applications to provide protective atmospheres or high vacuum at high temperature to eliminate contamination or impurity.

Chemical competent	Al2O3	≥85%
	SiO2	<12%
	Fe2O3	<0.5%
Alkaline matter		<2.5%
Density		2.6 g/cm3
Hardness		7 M
Water absorption		<0.2%
Rupture  strength		>1300kg/cm2
Gas tightness		Kept for ten minutes at negative pressure of 1.3Kpa. The pressure drop is less than 0.3Kpa.
Heat tolerance		Insert the pipe into the furnace at a depth of 20mm. Heat to 1600ºC and maintain for 30 minutes.
Alkali tolerance		In the Na2CO3 solution of 2N concentration, boil for 15 hours with the weight loss not greater than 20mg/dm2.
Volume resistance		>2*10(5) Ω·cm/1300ºC
Breakdown voltage		18kv/cm
Expansion coefficient		5*10(-8)
Temperature for use		Long-term: 1400ºC  Short-term: 1600ºC
Chill and abrupt heat		1300ºC~room temperature not cracking thric

4 holes Multibore insulators, suitable for thermocouples