Temperature classification is B. High mechanical property, stable dielectric property after immersing in water. Its a kind of current fabric laminate with excellent and comprehensive property. Used as slot and wedge of motors, the insulating structural parts for electric machine and apparatus equipment. Standard: GB/T1303.1-1998
Thickness : 0.5-80mm
Size: 1960mm*960mm, 1440mm*960mm
Table 1: Technical requirements
No | Property | Unit | Normal Value | |||||
1 | Flexural strength perpendicular to layer | At room temperature | MPa | ≥340 | ||||
150±2 | ||||||||
2 | Apparent flexural elastic modulus | MPa | ≥(24000) | |||||
3 | Compressive strength, perpendicular to layer | MPa | ≥350 | |||||
4 | Impact strength parallel to layer (Charpy method) | kJ/m2 | ≥33 | |||||
5 | Impact strength parallel to layer.(Cantilever beam method) | kJ/m | ≥34 | |||||
6 | Shear strength, parallel to the layer | MPa | ≥30 | |||||
7 | Tensile strength | Lengthwise | MPa | ≥(300) | ||||
Crosswise | ||||||||
8 | Electric strength,perpendicular to the layerat 90±2 oil. | MV/m | retail data see the standard | |||||
9 | Breakdown voltage, perpendicular to layer direction. | kV | ≥35 | |||||
10 | Dielectric constant | Under 48Hz62Hz | ≤5.5 | |||||
under1Hz | ≤5.5 | |||||||
11 | Dissipation factor | Under 48Hz62 Hz | ≤0.04 | |||||
Under 1MHz. | ≤0.04 | |||||||
12 | Insulation resistance after immersing in water. | W | ≥5.0×108 | |||||
13 | Comparative tracking index. | ≥200 | ||||||
14 | Heat resistance for long time. | ≥130 | ||||||
15 | Matin`s temperature | under consideration | ||||||
16 | Density | g/cm3 | 1.71.9 | |||||
17 | Water absorption | % | retail data see the standard | |||||
Note: The value in the parentheses for Type 3240 is typical value. Not used as the requirement only for reference. | ||||||||
Epoxy glass fabric laminate sheet