Product

 LDPE 

Resin Properities 

Test Result 

Melt Indexg/10min   

7~8

Densityg/ 12cm3' 

>0.922 

Tensile-strength 

Mpa9

Elongationat break

500% 

Softening pointVicat> 

 83°C 

Physical Properties

Test Method

Nominal Value

Unit

Density

ISO 1183

0.921

g/cm3

Melt Mass-Flow Rate (MFR)

ISO 1133

1.9

g/10min

Hardness

Shore Hardness (shore D)

ISO 868

45

Mechanical Properties

Tensile Modulus

ISO 527-2

175

MPa

Tensile Strength

Yield, 

ISO 527-2

9.0

MPa

Break,

13.0

MPa

Tensile Strain(Break)

ISO 527-2

850

%

Modulus of Elasticity

Internal Method

250

MPa

Thermal

Vicat Softening Temperature

ISO 306/A50

89.0

°C

Melting Temperature (DSC)

DIN 53765

108

°C

Peak Crystallization Temperature (DSC)

DIN 53765

97.0

°C

Heat of Fusion

DIN 53765

110

J/g

Electrical

Volume Resistivity

ASTM D257

8.5E+15

ohm •cm

Dielectric Strength

ASTM D149

30.0

kV/mm

Dielectric Constant (60Hz)

ASTM D150

2.20

%

Dissipation Factor (60 Hz)

ASTM D150

0.00050