The investment powder is applicable in (1)gold and lower melting temperature silver, (2 )brass and aluminum parts casting.

°cFeatures:1  High quality and low price, high performance/price ratio, can lower cost in a big scope for larger processing factories.2  The casting mold can bear temperature of 720°c(1328°F), and has higher thermal shock resistance. Casting mold can endure quick and direct temperature rising, while the mold cavity will not be fractured.3  Mold cavity duplicates are very clear and smooth. No apparent drop marks, metal beads and male-female face on casting surface.4  This investmetn powder is applicable in karat gold and lower melting temperature silver, copper-beryllium, brass and aluminum alloy jewelries and parts casting.5  Automatically collapsed when dip into water, easy to pattern drawing.

Model:	HK-1000
Water/Powder Ratio:	39-40:100
Working Time:	11-12 min
Initial Set Time:	13-16 min
Thermal Expansion @730:	0.78%
Setting Expansion @2hrs.:	0.60%
Thermal Compressive strength (730×1hrs):	0.62 MPa
Setting Compressive strength (2hrs.):	1.19 MPa
Max.Burnout Temp.:	720(1,328°F)

( function(){ var aBigImageSrc = [ 'http://i00.i.aliimg.com/photo/v19/226002408_1/Jewelry_Investment_Powder_of_HK_1000.jpg' , 'http://i00.i.aliimg.com/photo/v19/226002408_2/Jewelry_Investment_Powder_of_HK_1000.jpg' ]; var oProductShow = new AE.run.minisite.productShow(); oProductShow.init( { 'aImgSrc': aBigImageSrc } ); } )(); Jewelry Investment Powder of HK-1000