Steel wire hot dip galvanizing line 1.Material:Low,high carbon 2.Dia:0.5-12.5mm 3.Wires:8-40 4.Capacity:1,000-20,000 T/Y

Production process: Pay-off --> Alkali washing(Degreasing,Ultrasonic) --> Water washing --> Pickling washing (Ultrasonic pickling) --> Hot water cleaning --> Fluxing(Coat assisting) -->

Drying --> Hot-dip galvanizing --> Wiping system --> Take-up

Successfully apply Ultrasonic cleaning to our Steel Wire Hot-dip Galvanizing Continuous Line, replace the traditional degreasing and pickling process. Advantage: The solution can be recycled, no pollution to be discharged;To reach the same production capacity, the occupied area is less than traditional pickling bath; No acid mist in the workshop, safe for workers and reduce the damage to workshop.

 Technical parameter

Sr	Item	Specification
1	Raw material	Low, medium and high carbon
2	Wire diameter	Φ0.5mm-Φ12.5mm
3	Zinc thickness	60-350g/m2
4	Wire number	8-40 wires
5	Speed	10-120m/min
6	Production capacity	1000-20,000 tons/year
7	Energy	Natural gas, Liquid gas, Electricity, Diesel, Coal
8	Working hours	24h continuously
9	Line size	100m(L)x3m(W)x1(H)
10	Can be equipped with annealing furnace.

1. Fired directly annealing furnace:

 

2. Fumeless pickling and bathUltrasonic cleaning :

  

3. Hot dip galvanizing and Electro galvanizing for steel wire:

4. (Vertical spool)Pay-off and (Inverted)take-up machine:

Steel Wire Heat Treatment and Hot Dip Galvanizing Production Line