1.Fused type 2.Red brown to light yellow 3.Welding technology has good performance 4.25Kg/plastic woven bag 5.MOQ:1 Ton

Fit	GB/T5293-1999	F4A3-H08A	F5A2-H08MnA
Equivalent to	AWS-A5.17	F6A2-EL12	F7A3-EM12K

1.JN431 is a kind of high manganese and silicon, low fluorine fused flux

2.Color:red brown to light yellow

3.Grain size:of 8-40(2.5-0.45mm) and 14-40(1.5-0.45mm) meshes

4.Current:alternating or direct current (welding wires must be connected with the positive electrode when direct current is used)Usage:1.for low-carbon and low-alloy steels like 16Mn and 15MnV, as well as ships, boilers and high-pressure vessels[applied to welding wires such as H08A(AWS EL8), H08MnA(AWS EM12) and H10MnSi(AWS EM13K)] 2.for electro-slag and copper welding.Cautions:1.The oil stain, moisture, iron rust and other impurities must be removed from the surface2.Flux must be baked under 250~300°C for 2 hours before welding.Chemical Composition:(%) 

AL2O3 +MnO	CaO+MgO	SiO2	CaF2	FeO	S ,P
35~44	8~13	40~44	3~8	≤ 1.8	≤ 0.05

Mechanical Performance:Applied to H08A (AWS EL8)

Test item	Yield strength   6s (Mpa)	Tensile strength    6b (Mpa)	Elongation       δ5(%)	Impact absorption rate Akv  (-20°C)(J)
Common results	≥400	≥550	≥22	≥34

Fused welding flux