we are a factory which mainly produces flame-redundant nylon series products which are anti-high-temperature, environment-friendly, and of high strength and technology content. they are now widely used in various newly-emerging fields, including automobile, communication, electronics, electrical appliance, household appliance and sports products etc
Reinforced & Toughened PA6 with 30% glass fiber nylon6
polyamide injection grade
Performance | Test condition | Testing standard | Units | B2HG6 |
Mechanical property | ||||
Tensile strength | 5mm/min | ISO527-1/2 | Mpa | 155 |
Elongation at break | 5mm/min50mm/min | ISO527-1/2 | % | 3 |
Bending modulus | 2mm/min | ISO178 | Mpa | 7000 |
Bending strength | 2mm/min | ISO178 | Mpa | 220 |
Charpy notched impact strength | 23°C | ISO179/leA | KJ/m2 | 15 |
Charpy unnotched impact strength | 23°C | ISO179/leA | KJ/m2 | 70 |
Thermal | ||||
Melting | DSC.10K/min | ISO3146 | °C | 225 |
Heat distortion temp. A | 1.8Mpa | ISO75 | °C | 220 |
Heat distortion temp. B | 0.45Mpa | ISO75 | °C | 235 |
Electrical property | ||||
Surface resistivity | IEC60093 | Ohm | 1/0.1 | |
Volume resistivity | IEC60093 | Ohm×cm | 10/0.1 | |
Anti-arc-track of | TestotutionA | IEC60012 | V | |
Physical property | ||||
Density | 23°C | ISO1183 | g/cm3 | |
Hygroscopicity | 23°C,50%r.h | ISO62 | % | 1.0 |
Absorbent/water absorption | 23°C/saturtion | ISO62 | % | |
Radial shrinkage | flow | ISO294-4 | % | |
Transverse shrinkage | transverse | ISO294-4 | % | |
Flame retardant | ||||
Flammability test | 1.6/3.0mm | |||
The level of flame-retardant test | 1mm thickness | UL94 | ||
Material description | PA6+30%GF |