Super Tough,Very Flexible, Lubricated PA6 Offers High Productivity Low Temperature Toughness Down to -40 C SGS Inspection

ORACLE TM 5020T(B)  impact modified PA6 resin, Available in natural and black.Super Tough, high performance polyamide 6 resin. It offers outstanding molding performance in injection molding applications. High shock resistance even in the dry state and at low temperatures .

TEST ITEMS	TEST METHOD AND CONDITIONS			TEST RESULTS
	TEST METHOD	UNIT	CONTITIONS
			(DRY)23
Density	ISO1183	g/cm3		1.08
Melt Volume Rate	ISO1133	cc/10min	(275)2.16kg	5.4
Tensile Strength	ISO527	MPa	10mm/min	49
Tensile strain at break	ISO527	%		167
Flexural Strength	ISO178	MPa		49
Flexural Modulus	ISO178	MPa		1,500
Charpy Notched	ISO179	KJ/m2	2.9m/s-1J	38
Izod Notched Impact	ISO180	KJ/m2	3.5m/s-1J	51
Flame resistance	UL-94			HB
Ash content		%		0
Processing Guidelines
Material HandlingMax. Water content: 0.12% Product is supplied in sealed containers and drying prior to molding is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 °C (176 °F) is recommended. Drying time is dependent on moisture level, but 4-6 hours is generally sufficient
Typical ProfileMelt Temperature 220-250°C (428-482 °F) Mold Temperature 60-90 °C (158-194 °F) Injection and Packing Pressure 35-125 bar (500-1500 psi)
Fill RateFast fill rates are recommended to ensure uniform melt delivery to the cavity and prevent premature freezing. Surface appearance is directly affected by injection rate

nylon 6  nylon6

PA6