1-Rigid Foam Blend Polyols for Wood Imitation 2-Density range: 50kg/m3 to 900kg/m3 for different applications

Wood Imitation Rigid Polyurethane Blend Polyols 

           DFM-103H

Products Introduction

"Wood Imitation" structure foam , is a new type of carving synthetic materials. It has high mechanical strength and hardness, simple molding process , high production efficiency and excellent appearance. 

Characteristics are as follows,

1. excellent repetition molding property.  It not only can mould certain shape size, but also mould lifelike wood texture and other designs, good touch 

2. appearance and feel close to wood , which could be planed, nailed, drilled, and carved patterns or designs . 

3. Mold can be aluminum or steel, and silicon rubber, epoxy resin or other resins, which are low cost and easy machining. 

4. process is simple, fast, high efficiency of qualified. 

5. physical and mechanical properties is one of optimal synthesis wood produced by various polymer . Physical property can be controlled by adjusting the formula.

Physical Property

Appearance                Hydroxyl value                 mgKOH/g Viscosity          25°C        mPa.s Density           20 °C        g/ml Storage temperature            Storage stability                Month

Light yellow to brown yellow viscous liquid 250-400 1000-1500 1.10±0.02 10-25 6

Recommended Ratio

	pbw
DFM-103 polyols Isocyanate	100 60-100

Reactivity Characteristics Actual value varies as per processing conditions.

Rise time            s Gel time             s Tack free time        s Free density        kg/m3

50-70 140-160 200-220 300-850

Foam Performances

Moulding density   Curving  strength Compressive strength Tensile  strength Surface strength shrinking ratio

Kg/m3 MPa MPa MPa Shore D %

400-900 7-20 7-30 5-20 35-70 ≤0.1

Rigid Foam Blend Polyol for Wood Imitation