| Items | Unit | 930dtex/2 | 1400dtex/2 | 1870dtex/2 | 2100dtex/2 | |
| (840 D/2) | (1260 D/2) | (1680 D/2) | (1890 D/2) | |||
| Breaking Strength | N | MIN 135 | MIN 208 | MIN 275 | MIN 310 | |
| Elongation at Load | % | 9.5±0.8 | 9.5±0.8 | 9.5±0.8 | 9.5±0.8 | |
| (4.5KG) | (6.8KG) | (9KG) | (10.2KG) | |||
| Adhesion(H-Test) | N/CM | MIN 107.8 | MIN 137.2 | MIN 156.8 | MIN 166.6 | |
| Unevenness Of Strength | % | MAX 5.0 | MAX 5.0 | MAX 5.0 | MAX 5.0 | |
| Unevenness Of Elongation At Break | % | MAX 7.5 | MAX 7.5 | MAX 7.5 | MAX 7.5 | |
| Cord Gauge | MM | 0.55±0.04 | 0.65±0.04 | 0.75±0.04 | 0.78±0.04 | |
| Twist | Z twist | T/CM | 460±15 | 370±15 | 330±15 | 320±15 |
| S twist | 460±15 | 370±15 | 330±15 | 320±15 | ||
| Dip Pick Up | % | 4.5±1.0 | 4.5±1.0 | 4.5±1.0 | 4.5±1.0 | |
| Elongation At Break | % | 22±2 | 23±2 | 23±2 | 23±2 | |
| Moisture Content | % | MAX 1.0 | MAX 1.0 | MAX 1.0 | MAX 1.0 | |
| Heat Shrinkage | % | MAX 8.0 | MAX 6.5 | MAX 6.5 | MAX 6.5 | |
| Fabric Width | CM | M±2 | M±2 | M±2 | M±2 | |
| Items | Unit | 930dtex/1 | 1400dtex/1 | 1870dtex/1 | ||
| (840 D/1) | (1260 D/1) | (1680 D/1) | ||||
| Breaking Strength | N | MIN 67 | MIN 98 | MIN 127 | ||
| Elongation at Load | % | 7.5±1.0 | 7.0±1.0 | 8.0±1.0 | ||
| (2.3KG) | (3.4KG) | (4.5KG) | ||||
| Adhesion(H-Test) | N/CM | MIN 49 | MIN 64 | MIN 78 | ||
| Cord Gauge | MM | 0.32±0.03 | 0.43±0.03 | 0.50±0.03 | ||
| Twist | T/10CM | 21±1.5 | 19±1.0 | 16±1.0 | ||
| Dip Pick Up | % | 4.2±1.2 | 4.2±1.2 | 4.2±1.2 | ||
| Elongation At Break | % | 20±2 | 20±2 | 20±2 | ||
| Moisture Content | % | MAX 0.8 | MAX 0.8 | MAX 0.8 | ||
| Heat Shrinkage | % | MAX 4.0 | MAX 4.0 | MAX 4.0 | ||
| Fabric Width | CM | M±2 | M±2 | M±2 | ||
Polyester Dipped Tire Cord Fabric