1.biodegradable starch based plastic resin 2.environmental friend product 3.petroleum plastic added in to low the price

product properties

project	Testing method	Testing condition	Unite	Standard
Density	ASTM D1503-03	@23 °C	g/cm3	1.2-1.25
Melt-mess flow rate	ASTM D1238	v@190 °C, 2.16kg	g/10 min	1.2-2.5
Moisture content	ASTM D6980	@25 °C	%	Bellow 1.2
Tensile strength	ASTM D882	500mm/min	MPa	≥15
Breaking elongation	ASTM D882	500mm/min	%	≥250
Starch content	ASTM D6866		%	45%
Flexural strength	ASTM D790	2mm/min	MPa	45
Impact strength	ASTM D256	4mm @25 °C	KJ/M2	10
H.D.T	ASTM D648	1.8MPa.6.4mm	°C	58
Degradation rate	ASTM D6400 & EN13432	in 100 days	%	60

.

Product type

Biodegradable starch based plastic resin

Film blowing

Procession Technology

1.      the screw rotation should be slow at first, and then adjust the screw rotation faster to match the request.2.      fleshly blown film product feels a little brittle and scrip ,due to dehydration in production ,after 24 hours its function regain to normal plastics.3.      the preferred blow-up ratio is 1:2.5 or 3,the height from die of orifice to the nip roll should be higher than 2.5m which insure full cooling and prevent film blocking.

Applications:

  Plastic bags, packaging films ,shopping bags, food packaging, medical packaging.

biodegradable starch based plastic granule