Refractory Brick
Refractory Brick Magnesia Calcium Carbon Introduction:
Refractory Brick Magnesia Calcium Carbon is made from dolomite, magnesite, flake graphite as major material.
Characteristics:
1.High slag resistance
2.Excellent corrosion resistance,
3.Good thermal shock resistance,
4.Good thermal conductivity
5.Competitive price.
Application:
Magnesia Calcium Carbon Brick is mainly used in the converter, electric furnace.
1,Fireclay brick Chemical & Physical Index
| RI | A.P. | B.D. | C.C.S. | RUL | PLC(%) | |
| ≥(°C) | ≤% | ≥g/cm3 | ≥Mpa | ≥0.2Mpa°C | 1400°C×2h | 1350°C×2h |
N-1 | 176 | 22 |
| 300 | 1400 | 0.1~-0.4 |
|
N-2a | 174 | 24 |
| 250 | 1350 | 0.1~-0.5 |
|
N-2b | 174 | 26 |
| 200 |
| 0.2~-0.5 |
|
N-3a | 172 | 24 |
| 200 | 1320 |
| 0.2~-0.5 |
N-3b | 172 | 26 |
| 150 |
|
| 0.2~-0.5 |
N-4 | 170 | 24 |
| 200 | 1300 |
| 0.2~-0.5 |
N-5 | 166 | 26 |
| 150 |
|
| 0.2~-0.5 |
N-6 | 158 | 28 |
| 150 |
|
|
|
ITEM | STANDARD | |||||||
AL2O3(%) | 38 | |||||||
FE2O3(%) | 2.5 | |||||||
REFRACTORINESS(SK) | 34 | |||||||
REFRACTORINESS UNDER LOAD,0.2MPA,TA,() | 1350 | |||||||
POROSITY(%) | 19-23 | |||||||
BULK DENSITY(G/CM3) | 2.10-2.15 | |||||||
COLD CRUSHING STRENGTH(MPA) | 25 | |||||||
THERMAL EXPANSION AT 1000(%) | 0.6 |
Composition | Content(%) |
|
| ||
SiO 2 | 69.8 |
|
| ||
AL 2 O 3 | 21.5 |
|
| ||
K 2 O | 2.7 |
|
| ||
Na 2 O | 0.95 |
|
| ||
MgO | 0.12 |
|
| ||
CaO | 0.82 |
|
| ||
Fe 2 O 3 | 0.2 |
|
| ||
Burning loss | 0.54 |
|
| ||
Acid resistance | 99.8 |
|
|
refractory brick