typeproperties | Low aluminaball | Middle aluminaball | High aluminaball | CorundumAlumina ball | |
(%) | 20~25 | 47~56 | 90~92 | 98.5 | |
Al2O3+SiO2 (%)Min | 92 | 98.5 | |||
(%)Min | 1 | 0.2 | |||
CaO (%) Max | 1.5 | 2 | 3 | 0.2 | |
MgO (%) Max | 2.5 | 0.5 | 0.5 | 0.1 | |
K2 + Na2O | 4 | 3.5 | 4 | 0.5 | |
TiO2 (%)Max | 0.5 | 0.1 | 0.1 | 0.5 | |
Water absorption(%)Max | 3 | 01 | |||
Anti-acid (%)Min | 98 | ||||
Anti-alkali (%)Min | 80 | 85 | 90 | 95 | |
Density (g/cm3) | 2.3~2.4 | 2.6 | 3.5 | 3.0~3.6 | |
Spalling Resistance | 250 | 500 | 700 | 800 | |
Operation Temperature (oC) Max | 1100 | 1480 | 1760 | 1800 | |
Mohs Hardness Max | 6.5 | 7 | 7 | 7.5 | |
CrushingStrength(N/piece) | 6mm | 0.54 | 0.56 | 0.64 | 1 |
13mm | 1.56 | 1.67 | 1.99 | 3 | |
19mm | 2.89 | 4.21 | 3.21 | 5 | |
25mm | 4.89 | 6.22 | 5.28 | 8 | |
38mm | 5.33 | 8.92 | 5.33 | 8 | |
50mm | 6.22 | 9.8 | 8 | 15 |
refractory ceramic ball