Rigid Polyurethane Blend Polyols for Wood Imitation
DFM-103
Products Introduction
"Wood Imitation" structure foam , is a new type of carving synthetic materials. It has high mechanical strength and hardness, simple molding process , high production efficiency and excellent appearance.
Characteristics are as follows,
1. excellent repetition molding property. It not only can mould certain shape size, but also mould lifelike wood texture and other designs, good feel of touch
2. appearance and feel close to wood , which could be planed, nailed, drilled, and carved patterns or designs .
3. mould can only be produced using aluminum or steel, but can use silicon rubber, epoxy resin or other resin, which are low cost and easy machining.
4. process is simple, fast, high efficiency of qualified.
5. physical and mechanical properties is one of optimal synthesis wood produced by various polymer . Physical property can be controlled by adjusting the formula.
Physical Property
Appearance Hydroxyl value mgKOH/g Viscosity 25°C mPa.s Density 20 °C g/ml Storage temperature Storage stability Month | Light yellow to brown yellow viscous liquid 250-400 600-1000 1.10±0.02 10-25 6 |
Recommended Ratio
pbw | |
DFM-103 polyols Isocyanate | 100 100-105 |
Reactivity Characteristics
Actual value varies as per processing conditions.
Rise time s Gel time s Tack free time s Free density kg/m3 | 50-70 140-160 200-220 90-250 |
Foam Performance
Moulding density Curving strength Compressive strength Tensile strength Surface strength shrinking ratio | Kg/m3 MPa MPa MPa Shore D % | 300-600 7-20 10-20 10-25 50-80 ≤0.3 |
Polyols for Wood Imitation