duplex 2507 stainless steel sheet prime quality with competitive price sample availiable TPI before shipment MTC each order

duplex 2507 /S32507 1.4410 stainless steel sheet

General Properties

  Alloy 2507 (UNS S32750) is a super duplex stainless steel with 25% chromium, 4% molybdenum, and 7% nickel designed for demanding applications which require exceptional strength and corrosion resistance, such as chemical process, petrochemical, and seawater equipment. The steel has excellent resistance to chloride stress corrosion cracking, high thermal conductivity, and a low coefficient of thermal expansion. The high chromium, molybdenum, and nitrogen levels provide excellent resistance to pitting, crevice, and general corrosion.

The impact strength is also high. Alloy 2507 is not recommended for applications which require long exposures to temperatures above 570°F because of the risk of a reduction in toughness

Applications

Oil and gas industry equipmentOffshore platforms, heat exchangers, process and service water systems, fire-fighting systems, injection and ballast water systemsChemical process industries, heat exchangers, vessels, and pipingDesalination plants, high pressure RO-plant and seawater pipingMechanical and structural components, high strength, corrosion-resistant partsPower industry FGD systems, utility and industrial scrubber systems, absorber towers, ducting, and piping 

Standards           ASTM/ASME .......... A240 - UNS S32750           EURONORM............ 1.4410 - X2 Cr Ni MoN 25.7.4           AFNOR.................... Z3 CN 25.06 Az

Corrosion ResistanceGeneral CorrosionThe high chromium and molybdenum content of 2507 makes it extremely resistant to uniform corrosion by organic acids like formic and acetic acid. 2507 also provides excellent resistance to inorganic acids, especially those containing chlorides.

In dilute sulfuric acid contaminated with chloride ions, 2507 has better corrosion resistance than 904L, which is a highly alloyed austenitic steel grade specially designed to resist pure sulfuric acid.

Stainless steel of type 316L (2.5%Mo) cannot be used in hydrochloric acid due to the risk of localized and uniform corrosion. However, 2507 can be used in dilute hydrochloric acid. Pitting need not be a risk in the zone below the borderline in this figure, but crevices must be avoided.

Isocorrosion curves, 0.1 mm/year, in sulfuric acid with an addition of 2000 ppm chloride ions

Isocorrosion curves, 0.1 mm/year, in hydrochloric acid. Broken line curve represents the boiling point

Critical Pitting Temperature (CPT) range for various alloys in 1M NACl

Critical Crevice Corrosion Temperature (CCT)for various alloys in 10% FeCl3

Intergranural Corrosion 2507’s low carbon content greatly lowers the risk of carbide precipitation at the grain boundaries during heat treatment; therefore, the alloy is highly resistant to carbide-related intergranular corrosion.

Stress Corrosion CrackingThe duplex structure of 2507 provides excellent resistance to chloride stress corrosion cracking (SCC). Because of its higher alloy content, 2507 is superior to 2205 in corrosion resistance and strength. 2507 is especially useful in offshore oil and gas applications and in wells with either naturally high brine levels or where brine has been injected to enhance recovery.

Pitting Corrosion Different testing methods can be used to establish the pitting resistance of steels in chloride-containing solutions. The data above were measured by an electrochemical technique based on ASTM G 61. The critical pitting temperatures (CPT) of several high-performance steels in a 1M sodium chloride solution were determined. The results illustrate the excellent resistance of 2507 to pitting corrosion. The normal data spread for each grade is indicated by the dark gray portion of the bar.

Crevice CorrosionThe presence of crevices, almost unavoidable in practical constructions and operations, makes stainless steels more susceptable to corrosion in chloride enviroments. 2507 is highly resistant to crevice corrosion. The critical crevice corrosion temperatures of 2507 and several other high-performance stainless steels are shown above.

Chemical AnalysisTypical values (Weight %)

CCrNiMoNOthers
0.0202574.0.27S=0.001
PREN = [Cr%] + 3.3 [Mo%] + 16 [N%] ≥ 40

Mechanical PropertiesMechanical and Physical Properties 2507 combines high tensile and impact strength with a low coefficient of thermal expansion and high thermal conductivity. These properties are suitable for many structural and mechanical components. The low, ambient, and elevated temperature mechanical properties of 2507 sheet and plate are shown below. All of the test data shown are for samples in the annealed and quenched condition.

2507 is not recommended for applications which require long exposures to temperatures in excess of 570°F because of the increased risk of a reduction in toughness. The data listed here are typical for wrought products and should not be regarded as a maximum or minimum value unless specifically stated.

Mechanical Properties

Ultimate Tensile Strength, ksi116 min.
0.2% Offset Yield Strength 0.2%, ksi80 min.
0.1% Offset Yield Strength 0.2%, ksi91 min.
Elongation in 2 inches, %15 min.
Hardness Rockwell C32 max.
Impact Energy, ft.-lbs.74 min.

Low Temperature Impact Properties

Temperature °FRT34-4-40
Ft.-lbs.162162155140
Temperature °F-76-112-148-320
Ft.-lbs.11044307

Elevated Temperature Tensile Properties

Temperature °F68212302392482
0.2% Offset Yield Strength, ksi8065615855
Ultimate Tensile Strength, ksi116101989594

Physical Properties

Densitylb/in30.28
Modulus of Elasticitypsi x 10629
Coefficient of Thermal Expansion 68-212°F/°Fx10-6/°F7.2
Thermal ConductivityBtu/h ft °F8.7
Heat CapacityBtu/lb/°F0.12
Electrical ResistivityW-in x 10-631.5

ProcessingHot forming2507 should be hot worked between 1875°F and 2250°F. This should be followed by a solution anneal at 1925°F minimum and a rapid air or water quench.

Cold Forming Most of the common stainless steel forming methods can be used for cold working 2507. The alloy has a higher yield strength and lower ductility than the austenitic steels so fabricators may find that higher forming forces, increased radius of bending, and increased allowance for springback are necessary. Deep drawing, stretch forming, and similar processes are more difficult to perform on 2507 than on an austenitic stainless steel. When forming requires more than 10% cold deformation, a solution anneal and quench are recommended.

Heat Treatment2507 should be solution annealed and quenched after either hot or cold forming. Solution annealing should be done at a minimum of 1925°F. Annealing should be followed immediately by a rapid air or water quench. To obtain maximum corrosion resistance, heat treated products should be pickled and rinsed.

Welding2507 possesses good weldability and can be joined to itself or other materials by shielded metal arc welding (SMAW), gas tungsten arc welding (GTAW), plasma arc welding (PAW), flux cored wire (FCW), or submerged arc welding (SAW). 2507/P100 filler metal is suggested when welding 2507 because it will produce the appropriate duplex weld structure.Preheating of 2507 is not necessary except to prevent condensation on cold metal. The interpass weld temperature should not exceed 300°F or the weld integrity can be adversely affected. The root should be shielded with argon or 90% N2/10% H2 purging gas for maximum corrosion resistance. The latter provides better corrosion resistance.If welding is to be done on only one surface and post-weld cleaning is not possible, GTAW is suggested for root passes. GTAW or PAW should not be done without a filler metal unless post-weld cleanup is possible. A heat input of 5-38 kJ/in. should be used for SMAW or GTAW. A heat input of about 50kJ/in. can be used for SAW.

contacts:

Tianjin haohongweiye steel company

sales department

tel:86 22 86888678/26916110/26838043/86889936

fax:86 22 86888387

mobile: 86 15320151007 13512911799

www.stainless-steel-factory.com

duplex stainless steel sheet 2507

Ads by Google

About Us | Contact Us | Help | Terms & Conditions
Hot Products: A | B | C | D | E | F | G | H | I | J | K | L | M | N | O | P | Q | R | S | T | U | V | W | X | Y | Z | 0-9
Copyright Notice @ 2008-2013 ECVERY Limited and/or its subsidiaries and licensors. All rights reserved.