Ceramic tiles manufacturers moribi glossy tile 80x80cm 6L005
1 super glossy, nano 2 80x80cm3 water absorption less than 0.5%
Products Features:
1. Full body vitrified porcelain material fired under high temperature of 1200C.
2. Water absorption less than 0.5%.
3. Nano tech on surface with excellent ability of dirty-proof and super glossy.
4. High hardness, high strength and high antiwearing ability.
Technical Data | |||||
No. | Test Item | Unit | Technical Requirements | Test Result | |
1 | Size and Difference | mm | Length | 600±1.0 | 600.2~600.5 |
2 | Side straight | (%) | ±0.2 | -0.04 ~ +0.03 | |
3 | Right angle | (%) | ±0.2 | -0.04 ~ +0.05 | |
4 | SurfaceFlatness | (%) | Center curvature | ±0.2 | +0.04 |
(%) | Warpage | ±0.2 | -0.03 | ||
(%) | Side Curvature | ±0.2 | +0.04 | ||
5 | Surface Quality (Excellent class) | --- | No distinct surface defects of more than 95% of the tiles can be found by inspection at a distance of 0.8 meter above the tile surface | Conformed | |
6 | Water Absorption | (%) | Mean value ≤ 0.5Single value ≤ 0.6 | 0.10.09~0.1 | |
7 | Breaking strength | N | When the thickness is ≥ 9.5mm, the mean value shall be ≥1350 | 1635.8 | |
8 | Modulus of rupture | Mpa | Mean value ≥ 35Single value ≥ 32 | 39.037.1~40.0 | |
9 | Resistance to thermal shock | --- | No burst and crack appear after the test of resistance to thermal shock 10 times | Conformed | |
10 | Luster degress | --- | ≥ 55 | 57~59 | |
11 | Abrasion resistance | mm3 | ≤ 175 | 147 | |
12 | Resis to household chemical reagent | --- | Not lower than UB level | UA level | |
13 | Resistance to Acid | --- | Grade after being dipped into 3% Hydrochloric Acid for 12 days | ULA level | |
14 | Resistance to alkali | --- | Grade after being dipped into 30g/L potassium hydroxide for 12 days | ULA level | |
15 | Thickness |
|
| 9.0 - 11mm | |