TiNi memory alloy wire,NiTi shape memory wire,Nickel-Titanium shape memory alloy rod,Nickel Titanium wire,Nitinol wire
Nickel Titanium (also known as Nitinol) is the unique class of materials known as shape memory alloys,A thermoelastic martensitic phase transformation in the material is responsible for its extraordinary properties.These properties include the shape memory effect,supere;asticity,and high damping capability.The properties of Nitinol can be modified to a great extent by changes in alloy composition,mechanical working,and heat treatment.In most cases a trial and error process is required to optimize these factors for a particular application.
Baoji Lihua Non-ferrous Metals Co,.Ltd offers a wide variety of NiTi components to meet your unique requirements.In addition,many standard items are in stock.
Wire,Ribbon and bar
l Wire:diameters from 0.004”(0.1mm) to 0.080”(2mm) and above
l Bar:diameters from 0.080”(2mm) to 2.800”(70mm) and above
l Ribbon and Strip:from 0.001” * 0.002” (0.025mm * 0.05mm) to 0.030” *0.400” (0.75*10mm)
l Stranded Wire:many different configurations available
Steet:
l Thickness down to 0.004”(0.1mm)
l Width of about 1” to 8”(25 to 200mm)
l Length of about 4” to 80”(100 to 2000mm)
Tubing:
l Outer Diameter(O.D.) from 0.078” to 2”(2 to 50mm)
l Wall Thickness down to less than 0.004”(0.1mm) dependent upon O.D. size
Application:
It is widely used in chemical,medical,aviation,spacecraft,navigation,industry,communication,etc
Product Parameter:
Density | 6.45g/cm3 |
Melting Point | 1310°C |
Phase transtition temperature | -100°C to 100°C |
Modulus of elasticity | Martensite 28~41GPa |
Austenite 83 GPa | |
Hardness | Martensite 180Hv~200Hv |
Austenite 200Hv~350Hv | |
Yield Strength | Martensite 70Mpa~140Mpa |
Austenite 95Mpa~690MPa | |
Tensile Strenght | Annealed 850Mpa |
Melt processing 1900MPa | |
Elongation | Annealed 25%~50% |
| Melt processing 5%~10% |
The Maximum recovery stress | 600MPa |
NiTi Shape Memory Wire