PVC waterproofing membrane :
1.Property
1 Excellent weathering characteristics
2 high tensile strength and long-term flexibility
2 Specification
width :1-2.0mm
thinckness:1.5mm 1.8mm,2.0mm,
length:15m,20mm,25mm
code H, code L,code P ,code G
3. Technical date
GB/T12953-2003
Item | Specification | |||||||
H | L | P | G | GL | ||||
The resin thickness of Middle fabric mm≥ | — | 0.40 | ||||||
Tension cap | Maximum tension N/cm ≥ | — | 120 | 250 | — | 120 | ||
Tension strength Mpa≥ | 10 | 10 | ||||||
Maximum tension elongation %≥ | 15 | |||||||
Fracture elongation%≥ | 200 | 150 | 200 | 100 | ||||
Heat treatment size change rate %≤ | 2.0 | 1.0 | 0.5 | 0.1 | 0.1 | |||
Low-temperature bending | -25°CNo craze | |||||||
Water tightness | 0.3Mpa,2hNo seepage | |||||||
Attack resistance | 0.5kg·m,No seepage | |||||||
Static charge resistance | No seepage | |||||||
Seam peeling strength N/mm≥ | 4.0Membranes break | 3.0 | ||||||
right-angle tear strength,N/mm≥ | 50 | 50 | ||||||
Trapezoid tear strength N≥ | 150 | 250 | 220 | |||||
Water absorbing apacity(70°C 168h), % | After soaking≤ | 4.0 | ||||||
air-cure later≥ | -0.40 | |||||||
(80°C) Heat aging | time | 672h | ||||||
appearance | No craze, no bubble, no cohering, hole | |||||||
Tensile strength retention%≥ | 85 | |||||||
Elongation rate of keeping%≥ | 80 | |||||||
Cold bending Low temperature bend | No craze | |||||||
Chemistry resistance | appearance | No craze, no bubble, no cohering, hole | ||||||
Tensile strength retention %≥ | 85 | |||||||
%≥ Elongation rate of keeping | 80 | |||||||
Low-temperature bending | -20°C No craze | |||||||
Man-made climate quicken aging | time | 1500hb | ||||||
appearance | No craze, no bubble, no cohering, hole | |||||||
Tensile strength retention %≥ | 85 | |||||||
Elongation rate of keeping %≥ | 80 | |||||||
Low temperature bend | -20°C No craze | |||||||
PVC waterproofing membrane (CODE H)