Brazing is a process whereby a filler metal is heated above melting point and distributed between two or more close-fitting part

Brazing is a metal-joining process whereby a filler metal is heated above melting point and distributed between two or more close-fitting parts by capillary action. The filler metal is brought slightly above its melting (liquidus) temperature while protected by a suitable atmosphere, usually a flux. It then flows over the base metal (known as wetting) and is then cooled to join the workpieces together.It is similar to soldering, except the temperatures used to melt the filler metal are higher.

In order to obtain high-quality brazed joints, parts must be closely fitted, and the base metals must be exceptionally clean and free of oxides. In most cases, joint clearances of 0.03 to 0.08 mm (0.0012 to 0.0031 in) are recommended for the best capillary action and joint strength. However, in some brazing operations it is not uncommon to have joint clearances around 0.6 mm (0.024 in). Cleanliness of the brazing surfaces is also important, as any contamination can cause poor wetting (flow). The two main methods for cleaning parts, prior to brazing are chemical cleaning, and abrasive or mechanical cleaning. In the case of mechanical cleaning, it is important to maintain the proper surface roughness as wetting on a rough surface occurs much more readily than on a smooth surface of the same geometry.

Another consideration that cannot be overlooked is the effect of temperature and time on the quality of brazed joints. As the temperature of the braze alloy is increased, the alloying and wetting action of the filler metal increases as well. In general, the brazing temperature selected must be above the melting point of the filler metal. However, there are several factors that influence the joint designer's temperature selection. The best temperature is usually selected so as to: (1) be the lowest possible braze temperature, (2) minimize any heat effects on the assembly, (3) keep filler metal/base metal interactions to a minimum, and (4) maximize the life of any fixtures or jigs used. In some cases, a higher temperature may be selected to allow for other factors in the design (e.g. to allow use of a different filler metal, or to control metallurgical effects, or to sufficiently remove surface contamination). The effect of time on the brazed joint primarily affects the extent to which the aforementioned effects are present; however, in general most production processes are selected to minimize brazing time and the associated costs. This is not always the case, however, since in some non-production settings, time and cost are secondary to other joint attributes (e.g. strength, appearance).

 Flux

In the case of brazing operations not contained within an inert or reducing atmosphere environment (i.e. a furnace), flux is required to prevent oxides from forming while the metal is heated. The flux also serves the purpose of cleaning any contamination left on the brazing surfaces. Flux can be applied in any number of forms including flux paste, liquid, powder or pre-made brazing pastes that combine flux with filler metal powder. Flux can also be applied using brazing rods with a coating of flux, or a flux core. In either case, the flux flows into the joint when applied to the heated joint and is displaced by the molten filler metal entering the joint. Excess flux should be removed when the cycle is completed because flux left in the joint can lead to corrosion, impede joint inspection, and prevent further surface finishing operations. Phosphorus-containing brazing alloys can be self-fluxing when joining copper to copper.Fluxes are generally selected based on their performance on particular base metals. To be effective, the flux must be chemically compatible with both the base metal and the filler metal being used. Self-fluxing phosphorus filler alloys produce brittle phosphides if used on iron or nickel. As a general rule, longer brazing cycles should use less active fluxes than short brazing operations.

Filler materials

A variety of alloys are used as filler metals for brazing depending on the intended use or application method. In general, braze alloys are made up of 3 or more metals to form an alloy with the desired properties. The filler metal for a particular application is chosen based on its ability to: wet the base metals, withstand the service conditions required, and melt at a lower temperature than the base metals or at a very specific temperature.

Braze alloy is generally available as rod, ribbon, powder, paste, cream, wire and preforms (such as stamped washers). Depending on the application, the filler material can be pre-placed at the desired location or applied during the heating cycle. For manual brazing, wire and rod forms are generally used as they are the easiest to apply while heating. In the case of furnace brazing, alloy is usually placed beforehand since the process is usually highly automated. Some of the more common types of filler metals used are

Aluminum-siliconCopperCopper-silverCopper-zinc (brass)Gold-silverNickel alloySilverAmorphous brazing foil using nickel, iron, copper, silicon, boron, phosphorus, etc.

Welding Tips: What Is Brazing?

Related Products
Ads by Google

About Us | Contact Us | Help | Terms & Conditions
Hot Products: A | B | C | D | E | F | G | H | I | J | K | L | M | N | O | P | Q | R | S | T | U | V | W | X | Y | Z | 0-9
Copyright Notice @ 2008-2013 ECVERY Limited and/or its subsidiaries and licensors. All rights reserved.